Ite LF/VD Slag | Ladle Furnace Ihe mkpuchi Slag Pụrụ Iche maka Ịrụ Ọrụ Metallurgy nke Abụọ - Womic Steel Foto egosipụtara

Ite LF/VD Slag | Ladle Furnace Ihe mkpuchi Slag pụrụ iche maka igwe ígwè nke abụọ - Womic Steel

Nkọwa Dị Mkpirikpi:

Nha ite Slag:Ike ya bụ tọn 5 - 40 (dakọtara na olu LF slag nkịtị), ịdị arọ ya bụ tọn 8 - 45, olu ya bụ tọn 4 - 25 m³, nha ya bụ nke ahaziri maka ikpo okwu ọrụ ọkụ ladle na ụzọ ọnụ ụzọ slag. Trunnion: Nhazi dị ala nke nwere nhazi dị mfe iji mee ka ladle dị ọcha.

Ihe na Ụkpụrụ:ZG270-500+ (S≤0.012%, P≤0.015%), GS-20Mn5V (nwere vanadium), ọkwa obere hydrogen ASTM A27 65-35. Dabara na ASTM A27, DIN 17182, EN 10293, ISO 3755. Ọgwụgwọ okpomọkụ: Emechara emenyụ + na-eme ka mmiri ghara ịdị ọcha + na-eme ka mmiri ghara ịdị ọcha. Elu: ime nwere profaịlụ radius dị nro iji nyere aka na mmiri simenti sịntetik, mpụta nwere mkpuchi dị elu maka oyi redioaktivu.

Usoro Mmepụta:Ihe mejupụtara otu ihe eji eme ihe, nke nwere nlebara anya pụrụ iche na oke gas maka ọrụ VD. EAF + LF + VD + degassing ogologo oge (H < 1.5ppm). Nlereanya okpomọkụ-mmiri CAE maka iwepụ ihe mkpofu. 100% NDT: UT olu zuru oke (Ọkwa 1, ahụ ọkwa 2), MT, PT, tinyere ule ntapu helium maka ọrụ vacuum.

Ojiji ite Slag:Njikwa ihe eji eme ka ọkụ ladle (LF) rụọ ọrụ, nchịkọta ihe eji eme ka ọ ghara ịdị ọcha nke VD/VOD, mbupu ihe eji eme ka ọ ghara ịdị ọcha site na ọdụ ígwè nke abụọ, nhazi ígwè alloy, ụlọ ọrụ ígwè pụrụ iche (ígwè na-ebu ígwè, ígwè pipeline, ígwè spring), njide ihe eji eme ka ọ ghara ịdị ọcha nke AOD, njikọta sistemụ nchọpụta ihe eji eme ka ọ ghara ịdị nkọ.

Womic Steelna-enye ite slag nke LF/VD nke nwere obere hydrogen dị elu (≤1.5 ppm) iji gbochie mgbawa nke hydrogen kpatara n'okpuru oghere ikuku. Redi anyị dị nro na-ewepụ ebe ndị nwụrụ anwụ ebe slag sịntetik nwere ike ịchịkọta. Nhazi ahaziri maka nhazi ụlọ elu ọkụ ladle ọ bụla. Asambodo ISO 9001, PED, NORSOK M-650 maka asambodo. Rịọ maka asambodo ndakọrịta vacuum.

Zitere anyị ozi-e Nkọwapụta Ngwaahịa

Nkọwa Ngwaahịa

Akara Ngwaahịa

Nchịkọta Ngwaahịa - Ihe Pụrụ Iche A Na-achọ n'Ime ite LF/VD Slag

A ite LF nke a na-akpọ slag(ihe e ji etinye ihe mkpuchi ọkụ n'ọkụ) ma ọ bụIte VD slagaka (bọket oghere nke na-agbaze ihe ikuku)ihe e ji sịntetik mee– ọ bụghị ihe e ji eme ihe ike, nke nwere oke okpomọkụ sitere na EAF ma ọ bụ BOF, kama ọ bụ ngwakọta nke lime, fluorspar, na alloys ejiri nlezianya gwakọta iji mee ka ígwè gbazee mma.

Gịnị mere ite LF/VD ji dị iche?

1. Okpomọkụ slag dị ala (~1,500°C vs 1,650°C maka EAF), mana oge ijide ya dị ogologo karịa– mgbe ụfọdụ nkeji iri isii ruo iri itoolu n'otu okpomọkụ. Ite ahụ aghaghị iguzogidemgbanwe na-asọ asọna okpomọkụ dị elu na-adịgide adịgide.

2. Slag sịntetik na-agba mmiri nke ukwuu mgbe ọ gbazere agbaze mana ọ na-arapara nke ukwuu ka ọ na-ajụ oyi.Ebe ndị nwụrụ anwụ ma ọ bụ akụkụ dị nkọ dị n'ime na-akpata mmụba nke slag nke na-ebelata ikike ka oge na-aga.

3. Mkpọpụ ikuku (VD) na-etinye ihe pụrụ iche achọrọ: a pụrụ itinye ite ahụ n'okpuru oghere ikuku (0.5–1 torr) ruo obere oge. Obere porosity ọ bụla dị na ihe e ji amị ihe nwere ike ịpụ apụ na gas, nke na-eduga nanhazi afụ n'ime ígwè ahụma ọ bụ - ka njọ -itinye ite ahụọ bụrụ na oghere buru ibu dị.

4. A na-ejikwa otu ihe e ji ebuli ihe e ji ebuli ihe e ji ígwè rụọ arụ ọrụ na ite LF/VD.Nke a pụtara na ite ahụ ga-adị mfe ma dị obere karịa ite EAF/BOF iji dabara n'ime oghere aka turret na geometry nke kreen.

5. Kemistri Slag bụ ihe dị mfe (CaO2/Al₂O2) nke na-awakpo ókèala mkpụrụ silikọn na aluminom.Ọ dị mkpa ka a lebara ihe ndị na-abụghị nke ígwè anya nke ọma.

E ji ite LF/VD nke Womic Steel rụọ ọrụ.obere ọdịnaya haịdọn, njupụta dị n'ime dị nro, nankenke obere akụkụ- kpọmkwem ihe ọrụ ígwè nke abụọ chọrọ.

LFVD Slag Pot Ladle Furnace Pụrụ Iche Slag Container maka Secondary Metallurgy – Womic Steel

Gịnị mere ị ga-eji họrọ Womic Steel maka ite LF/VD Slag?

Ihe achọrọ	Ngwọta Womic
Ọdịnaya haịdrọjin ≤1.5 ppm	Mbelata ugboro atọ: VD mgbe agbazechara, VD mgbe emechara ka ọ dị ọcha, tinyere mwepụ nke mmiri mmiri n'oge ọgwụgwọ okpomọkụ (awa 48 na 650°C).
Ike ịgbọ agbọ na 1,500°C (2,730°F)	Ọdịnaya Mo dị elu (0.4–0.6%) na ọkwa alloy, tinyere ike nke ngwọta site na iji vanadium.
Enweghị ebe ndị nwụrụ anwụ na-egbu ahịhịa	Profaịlụ dị n'ime nwere naanị radii > 50mm; anyị CNC-igwe mgbanwe mpaghara iji wepụ cusps.
Ndakọrịta ihe mkpofu	Nnwale UT + helium nke nwere olu 100% na-eme ka ọ ghara inwe porosity jikọtara ọnụ. Asambodo nke <1e-6 mbar·l/s.
Dị fechaa mana siri ike	Okpukpu mgbidi kachasị mma site na FEA (nkezi 40–50mm vs 60–70mm maka ite EAF); ibu belatara 25% na-enweghị ike ịla n'iyi.
Mwepụ nke slag dị nro	Mkpuchi ịsa ákwà seramiiki (ọ bụghị mkpuchi zuru oke) + mmecha elu a na-egbuke egbuke (Ra ≤ 3.2 μm).
Tret dabara	Anyị na-enyocha ogwe aka ụlọ ọkụ ladle gị site na laser ma na-enye ụdị 3D iji chọpụta na e kewapụrụ ya tupu e mee ya.

Anyị na-enyekwanha njikọta slag n'ebe ahụ– anyị na-etinye ibu arọ e kenyere n'ime ite ahụ, kpoo ya ọkụ ruo 1,200°C, ma tụọ ike achọrọ iji gbajie slag.

Nkọwapụta Nkà na ụzụ - ite Slag kachasị mma nke LF/VD

Ntụaka Nha Ike vs. Ladle

Ike Ladle nke ígwè (ton)	Olu LF Slag nkịtị (tọn)	Ike ite akwadoro (ton)	Ibu ite (ton)	Dia mpụta (mm)	Ogologo (mm)
60	4-6	6-8	9-12	1,200	900
80	6-9	10-12	14-18	1,350	1,050
100	8-12	12-15	18-22	1,500	1,150
120	10-15	15-20	22-28	1,600	1,250
150	12-18	20-25	28-34	1,700	1,350
180	15-22	25-30	Afọ 34-40	1,800	1,450

Nha ite ahụ ga-adaba na ụlọ elu ọkụ ladle - anyị na-emeziwanye ya dịka akụrụngwa gị si dị.

Ọkwa ihe maka ọrụ LF/VD

Ọkwa	Atụmatụ Pụrụ Iche	Ebumnuche ọdịnaya H	Ike Ịrịgharị (1,500°C, awa 100)	Kachasị mma maka
ZG270-500 Ultra-Low H	S≤0.012%, P≤0.015%, ikuku ikuku gbapụrụ	≤1.8 ppm	25 MPa	Igwe carbon nkịtị LF
GS-20Mn5V (+V)	Vanadium 0.10-0.20% maka iguzogide creep	≤1.5 ppm	35 MPa	Ígwè alloy, ígwè na-ebu ibu
ASTM A27 65-35 Obere H	Site na Cu+Ni+Mo, ọgwụgwọ mmiri mmiri	≤1.2 ppm	40 MPa	Ígwè pụrụ iche, alloy dị elu
1.5415 (16Mo3) gbanwere	Mo 0.25-0.35%, Cr 0.30% kachasị	≤1.2 ppm	55 MPa	Oke nguzogide na-agagharị agagharị (VD dị arọ ọrụ)

Ihe mgbaru ọsọ nkịtị:Maka ọtụtụ ngwa LF, GS-20Mn5V na-enye nguzozi kacha mma. Maka VD (vacuum), anyị na-akwado ASTM A27 65-35 Low H ma ọ bụ 16Mo3 agbanweela.

Data Nnwale Mberede (Nwanyị dị n'ime)

ihe	Okpomọkụ	nrụgide	Oge mmebi (etiti)	Ogologo oge mgbe mgbawa gasịrị
GS-20Mn5V	1,500°C	30 MPa	Awa 210	Pasentị iri na abụọ
Ụdị ASTM A27	1,500°C	40 MPa	Awa 165	8%
16Mo3 mod	1,500°C	50 MPa	Awa 98	6%

*Ọnọdụ ndị a karịrị ihe achọrọ maka ite LF slag nkịtị (ọ na-abụkarị awa 2-3 na oke okpomọkụ kachasị maka okpomọkụ ọ bụla).*

Usoro Mmecha Hydrogen (maka Ọrụ Uku)

Ogbo egwuregwu	Okpomọkụ	Oge	Ikuku	Ebumnuche
1	350°C	awa iri na abụọ	Ikuku	Mwepụ mmiri mbụ
2	550°C	awa iri abụọ na anọ	N₂ akọrọ	Mgbasa nke hydrogen atọm
3	650°C	awa iri anọ na asatọ	N₂ akọrọ + 5% H₂ onye na-enweta ya	Mbelata mmiri mmiri dị omimi
4	300°C (ọkụ dị jụụ)	awa 10	N₂ akọrọ	Gbochie mmịghachi ọzọ

Ihe nyocha LECO kwadoro ọdịnaya hydrogen ikpeazụ (ihe nlele sitere na isi trunnion).

Profaịlụ Dị n'ime Maka Mmiri Slag Sịntetik

Mpaghara	Ndago	Redịọs	Mmecha elu	ọrụ
Akụkụ elu	5° n'ime	75mm	Ejiri igwe rụọ ya, Ra 6.3	Ntuziaka ntinye Slag
Ahụ elu	8° taper	Na-aga n'ihu 50mm	Ejiri igwe rụọ ya, Ra 3.2	Isi ihe na-agbadata slag
Ahụ dị ala	6° taper	Na-aga n'ihu 60mm	A na-eme ka ọ dị ọcha, Ra 1.6	Ọsọ ọsọ maka mwepụta
Ala	Hemispherical	R = 150mm	A na-eme ka ọ dị ọcha, Ra 1.6	Enweghị mpaghara ebe a na-akwụsị akwụsị

Elu ime dị nro ma dị mma nke ejikọtara ya na ịsa ákwà seramiiki na-ebelata njikọta slag site na ihe dị ka 70% ma e jiri ya tụnyere elu as-cast.

Ite Slag nke nwere ike ibu ihe dị ka tọn 20-50 maka ime ígwè EAF na LF – Womic Steel

Njikwa Ogo maka ite LF/VD Slag - Nchekwa Vacuum & Creep

Ule	Ụzọ	Nnabata
Ọdịnaya haịdrọjin	Ihe nyocha ọkụ LECO	≤1.5 ppm (ma ọ bụ dịka akọwapụtara)
Nnwale ntapu helium	Ụlọ ikuku ọkụ + igwe nlele oke	Ọkwa ntapu < 1×10⁻⁶ mbar·l/s
Ultrasonic (olu zuru oke)	Usoro nhazi + TOFD	Enweghị ntụpọ planar>3mm; porosity klas 2 kachasị
Nnwale ịkpa ike (nhọrọ)	Ibu na-aga n'ihu na 1,500°C	Mgbawa > 100h na 40 MPa
Akụkụ (dabara na turret)	Nyocha laser + ntụnyere CAD	Enweghị nnyonye anya; enyochala nleghara anya
Trunnion UT	Dịka ASME V si dị, tinyekwara oghere nkuku	Enweghị ihe ngosi ahịrị> 1.5mm
Nnwale mwepụta slag	Ụdị nha nwere slag ígwè	Ihe fọdụrụ n'ime slag <5%

01 20-50 Ton Slag Ite Ike Ọkara Slag Ladle maka EAF na LF Steel Making – Womic Steel

Usoro Mmepụta - Vacuum & Creep Dakọtara

1. Nhọrọ ihe- obere P, obere S ígwè mkpofu + ígwè ezi, enweghị ihe mkpofu a na-atụgharịgharị ọzọ.

2. Ịgbaze EAF + ime ka LF dị ọcha– S<0.010%, P<0.012%, ọgwụgwọ Ca.

3. Mkpọpụ ikuku (VD) na 0.5 torr– jide ya ruo nkeji iri abụọ na ise, wepụ H ruo <1.5 ppm.

4. Mwụda ala– otu laịd n'ime ebu, nke a na-achịkwa nke ọma (1,550–1,570°C).

5. A na-achịkwa oyi n'ebu- awa iri anọ na asatọ tupu ịma jijiji iji zere obere mbelata.

6. Nhicha na igweri mbụ- wepụ ihe mkpuchi, oghere.

7. Ọgwụgwọ okpomọkụ ngwọta– 950°C, jide awa abụọ kwa 25mm, ikuku a na-emenyụ emenyụ.

8. Ime achịcha na-ebelata mmiri mmiri- dịka tebụl protocol dị n'elu si dị.

9. Na-eme ka ahụ dị jụụ- 600°C, jide awa 4, ikuku jụrụ oyi.

10.Ịrụ ọrụ siri ike- okirikiri ala, oghere trunnion.

11.NDT (UT, MT, PT, ule ntapu mmiri)- ọ bụla ịjụ na-akpalite mmegharị ọzọ.

12.Nhazi ikpeazụ- profaịlụ dị n'ime ya na CNC, na-enweta Ra 3.2.

13.Ngwa ịsa ákwà seramiiki– fesa ya, kpoo ya n'ikuku, wee gbaa ya ọkụ na okpomọkụ 400°C.

14.Akụkọ na akara akụkụ ikpeazụ.

02 20-50 Ton Slag Ite Ike Dị Mfe Maka Ịmepụta Steel EAF na LF – Womic Steel

Nkwakọ ngwaahịa maka ite LF/VD Slag (Ọ dị mma maka ịdị ọcha)

Ebe ọ bụ na a pụrụ iji ite LF/VD slag mee ihe n'ime ihe mkpofu, anyị na-ezere mmanụ ndị e ji hydrocarbon mee. Kama:

● E ji igwe echekwa elu yaihe nkiri plastik VCI (VCI), ọ bụghị mmanụ.

● Emechiri n'imeakpa ihe mkpofu(nhọrọ) ọ bụrụ na achọrọ maka ọrụ nhicha ikuku dị mkpa.

● Igbe osisi e ji ígwè mee ka ọ sie ike, nke e ji ihe na-ekpochapụ ihe n'ime ya.

● Mbupu site na ibu ụgbọelu maka nnọchi ngwa ngwa (ibu ite ahụ dị ihe dịka kilogram 1,500 maka obere nha).

Ọmụmụ Ihe - ite LF/VD Slag na-arụ ọrụ

Ikpe nke 1: Ụlọ Ọrụ Mearing Steel, Japan – Mgbochi Mgbawa Hydrogen

Ihe ịma aka:Ite ndị e ji mee ihe n'usoro VD nwere mgbawa mgbe ọnwa 18 gachara n'ihi chaja hydrogen.
Ngwọta:Womic nyere ite ASTM A27 nwere obere hydrogen (H≤1.2ppm) na mmiri mmiri na-adịghị na haịdrojineation.
Nsonaazụ:Ọnwa iri atọ na isii ma ọ ka na-enweghị mgbawa. Mee otu ihe ahụ maka ite iri abụọ.

Ikpe nke Abụọ: Ụlọ Ọrụ Nrụpụta Ihe Ọkụ Pipeline, Germany – Mgbanwe Ọkpụkpụ

Ihe ịma aka:Ite LF nke e ji ihe mkpuchi mee dara n'akụkụ ya mgbe afọ abụọ gachara, nke mere ka e nwee ntụpọ na ụlọ elu ahụ.
Ngwọta:16Mo3 nke ejiri Mo dị elu gbanwee, tinyere ọkpụrụkpụ mgbidi ya mụbara site na 8mm.
Nsonaazụ:Enweghị mgbanwe a na-ahụ anya mgbe afọ atọ gachara. Onye ahịa nakweere Womic dị ka onye na-ebunye ya ihe.

Ikpe nke 3: Specialty Steel LF, USA – Slag Freeze-on

Ihe ịma aka:Ihe fọdụrụ n'ime slag e ji sịntetik mee belatara ikike ịrụ ọrụ nke ọma site na 30% n'ime ọnwa isii.
Ngwọta:Profaịlụ ime a kpụchara akpụcha (Ra 1.6) + ákwà seramiiki a kpụchara akpụcha.
Nsonaazụ:Mfu ikike <5% mgbe ọnwa iri na abụọ gachara. Oge a na-atụfu slag belatara pasentị iri anọ.

05 20-50 Ton Slag Ite Ike Dị Mfe Maka Ịmepụta Steel EAF na LF – Womic Steel

Ngwa - Ebe ite LF/VD Slag dị oke mkpa

●Ọdụ ọkụ ladle (LF)- maka ígwè alloy, ígwè ngwaọrụ, ígwè na-ebu ígwè

●Ihe mkpofu ikuku (VD / VOD)- gụnyere akara igwe anaghị agba nchara

●Ịgafe ihe e ji atụ ladle slagsite na nchacha ruo na slag ground

●Ụlọ ọrụ ígwè pụrụ icheimepụta ígwè dị ọcha nke ukwuu (ụgbọelu, ọkpọkọ mmiri)

●Ụlọ ọrụ nyocha na nnwale- obere ite slag (1-5 tọn)

Ajụjụ Ndị A Na-ajụkarị (Ajụjụ Ndị A Na-ajụkarị) – LF/VD Pụrụ Iche

Ajụjụ: Gịnị mere ọdịnaya hydrogen ji dị oke mkpa maka ite slag?
A: N'oge a na-ewepụ gas ikuku, hydrogen agbazere agbaze n'ime ihe e ji kpụọ ígwè nwere ike ịgbasa ma jikọta ya ọzọ ka ọ bụrụ hydrogen molekul na ihe ndị na-abụghị ọla. Nke a na-emepụta nrụgide dị n'ime, na-ebute ọnya ma ọ bụ mgbawa - nke a na-akpọ mgbe ụfọdụ "mgbawa hydrogen." Ite LF/VD nwere ike ịdị ize ndụ n'ihi na a na-ejide ha n'okpuru vacuum ruo ogologo oge.

Q: Ị nwere ike ịkwado ọdịnaya hydrogen ka ọ bụrụ <1.0 ppm?
A: Ee, mana ọ chọrọ usoro ịgbaze pụrụ iche (ịgbaze induction vacuum ma ọ bụ ịgbaze electroslag) ma na-efu ihe karịrị. Maka ọtụtụ ojiji, 1.5 ppm zuru oke.

Q: Ị na-enye nnwale mmiri mgbapụta?
A: Ee, anyị na-eme nnwale mmiri helium ma ọ bụrụ na anyị arịọ ya ma nye anyị asambodo dịka ISO 20485 si kwuo. Anyị na-ekwe nkwa ọnụego mmiri <1×10⁻⁶ mbar·l/s.

A: Ugboro ole ka a ga-agbanwe ite LF slag?
A: Ọ na-abụkarị kwa afọ 3-5, dabere na okirikiri. Mgbanwe nke creep bụ ihe na-egbochi ndụ. Nnyocha UT kwa afọ nwere ike ịchọpụta oghere ndị na-apụta n'oge.

A: Ị nwere ike inye ite ndị e ji slag mee ihe na jaket ikuku oyi?
A: Maka ngwa LF nke chọrọ ka oyi dị ngwa ngwa tupu ejiri ya ọzọ, anyị nwere ike imepụta jaket ikuku dị mkpa (akpụkpọ mpụta ígwè nwere ọwa ikuku). Nke a na-ebelata oge oyi site na nkeji iri itoolu ruo nkeji iri abụọ.

A: Ite LF gị ọ dakọtara na sistemụ nchọpụta ọkwa slag akpaka?
A: Ee. Anyị na-enye ihe mkpuchi dị larịị n'elu rim maka radar ma ọ bụ ihe mmetụta laser. Ma ọ bụghị ya, anyị nwere ike itinye thermocouples maka nchọpụta oyi akwa slag.

A: Ị na-enye ọzụzụ maka inyocha ite LF?
A: Ee, anyị na-enye ọzụzụ otu ụbọchị n'ebe a na-arụzi ihe maka ndị otu gị: UT nke trunnions, njirisi nlele anya, na usoro ndozi mgbawa.

Q: Kedu ihe bụ akwụkwọ ikike nkịtị maka ite LF/VD slag?
A: Ọnwa iri abụọ na anọ ma ọ bụ okirikiri iri - nke ọ bụla buru ụzọ bịa. Maka ọrụ ikuku (na nnwale mmiri), a na-agbatị akwụkwọ ikike ruo ọnwa iri atọ na isii megide mgbawa hydrogen.